Incoloy Alloy 800 chinhu chinoshandiswa zvakanyanya chigadziriso chemidziyo inofanirwa kuve nesimba rakawanda uye kuramba oxidation, carburizing uye zvimwe zvinokuvadza zvekuratidzwa kwekushisa kwepamusoro (yepamusoro tembiricha yekushandisa inoda yakakwana inokambaira uye kuputsika zvivakwa, shandisa Incoloy Alloy 800H uye 800HT).
Alloy | % | Ni | Cr | Fe | C | Mn | Si | Cu | S | Al | Ti | Al+Ti |
Inhamba 800 | Min. | 30 | 19 | balance | - | - | - | - | - | 0.15 | 0.15 | 0.3 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 | ||
Incoloy 800H | Min. | 30 | 19 | balance | 0.05 | - | - | - | - | 0.15 | 0.15 | 0.3 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 | ||
Incoloy 800HT | Min. | 30 | 19 | balance | 0.06 | - | - | - | - | 0.25 | 0.25 | 0.85 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 |
Density (g/cm3) | Melting point (℃ ) | Elastic modulus (GPa) | Thermal conductivity (λ/(W(m•℃)) | Thermal kuwedzera coefficient ( 24 -100°C)(m/m °C) | Kushanda tembiricha (°C) |
7.94 | 1357-1385 | 196 | 1.28 | 14.2 | -200 ~ +1,100 |
Alloy | Form | Condition | Ultimate Tensile simba kisi (MPa) | Goho rinosimba pa 0.2% offsetkisi (MPa) | Elongation mu2″kana 4D, muzana |
800 | Sheet, Plate | Annealed | 85 (586) | 40 (276) | 43 |
800 | Sheet, Plate Strip, Bar | Annealed | 75 (520)* | 30 (205)* | 30* |
800H | Sheet, Plate | SHT | 80 (552) | 35 (241) | 47 |
800H | Sheet, Plate Strip, Bar | SHT | 65 (450)* | 25 (170)* | 30* |
Bar/Rod | Waya | Strip/Coil | Sheet/Ndiro | Pipe/Tube | Fitting |
ASTM B 408 uye SB 408 | ASTM B408, AMS 5766, ISO 9723, ISO 9724, BS 3076NA15, BS 3075NA15, EN 10095, VdTüV 412 & 434, AWS A5.11 ENiCrFe-2, AWS-ERNi A5.1. | ASTM B 409/B 906, ASME SB 409/SB 906, ASME Code Case 1325, 2339 | ASTM B409, AMS 5877, BS 3072NA15, BS 3073NA15, VdTüV 412 & 434, DIN 17460, EN 10028-7, EN 10095 | ASTM B 163/ SB 163 | ASTM B366 |
• Yakanakisa corrosion resistance mumidhiya yemvura yekupisa kwakanyanya kwe500℃.
• Good stress corrosion resistance
• Kugadzira kwakanaka
• High simba rinokambaira
• Kuramba kwakanaka kwazvo kune oxidation
• Kuramba kwakanaka kumagasi ekupisa
• Kuramba kwakanaka kwazvo kune carburization
• Kuramba kwakanaka kwenitrogen kunwisa
• Kugadzikana kwakanaka kwemaitiro pakupisa kwakanyanya
• Weldability yakanaka
• Ethylene choto kudzima boilers• Kuputika kweHydrocarbon
• Mavharuvhu, mafittings uye zvimwe zvikamu zviri pachena kune corrosive attack kubva 1100-1800° F.
• Zviviro zveindasitiri• Michina yekupisa kupisa
• Kemikari uye petrochemical processing • Heat exchangers
• Super-heater uye re-heater mumagetsi emagetsi • Kumanikidza midziyo